DLP printing of viscoelastic hydrogel/calcium phosphate composites for bone tissue replacement

Preobrazhensky, I.I.; Tikhonov, A.A.; Evdokimov, P.V.; Putlyaev, V.I.

Авторы: Preobrazhensky I.I., Tikhonov A.A., Evdokimov P.V., Putlyaev V.I.
Сборник: Conference Abstracts yCAM 2020 (young Ceramists Additive Manufacturing Forum), 2020 October 28-30, 2020 Online conference in gather.town
Тезисы
Год издания: 2020
Место издания: European Ceramic Society Берлин-Рим
Первая страница: 40
Последняя страница: 40
Аннотация: 3D-printing, and more specific, stereolithography, is a promising technique to fabricate materials for the restoration and regeneration of different tissues. Photopolymerization of different materials underlying the technique and combining biodegradable, osteoconductive, osteoinductive and required mechanical properties, allowing easily managing architecture and macroporosity of the material, is very attractive for regenerative medicine purposes. All of the parameters are extremely significant in the case of bone healing implants. This work was aimed at obtaining of viscoelastic hydrogel/calcium phosphate composites with complex architecture («gyroid»-type) through DLP 3D-printing assuming personalized bone tissue regeneration. Hydrogels based on polyethylene glycol derivatives (PEG-diacrylate or PEGDA (M=575 Da), PEG-methacrylate or PEGMA (M=350 Da)), were chosen as one of the most commonly used and biocompatible synthetic polymers for biomedical applications, with adjustable viscoelastic mechanical and swelling properties, and applicable for DLP printing. Reinforcement and functionalization of hydrogel matrices were carried out by filling with calcium phosphates with various micromorphology and resorbability, viz. brushite (СаНРО4•2Н2О), octacalcium phosphate (Са8(НРО4)2(РО4)4•5Н2О, OCP), or ceramic particles of tricalcium phosphate (Са3(РО4)2, TCP). Such biocomposites were obtained through light exposure with UV-lamp or with 3D-printer Ember (Autodesk, USA) of the slurries containing biocompatible photoinitiator Irgacure® 819 (BASF, Germany). Based on the results of the work, the optimal ratio of the monomers and the filling fraction of calcium phosphates in hydrogels were found. It was shown that the increase of methacrylate content allows obtaining composites with a higher swelling ability (up to ca. 4 times in terms of mass gain) and faster biodegradation behavior. Reinforcement of the hydrogels with the calcium phosphate particles led to greater stiffness as well as to the growth of the phase shift between shear loss and storage modules. The work was supported by RSF, grant №17-79-20427. The authors acknowledge partial support from Lomonosov Moscow State University Program of Development
Добавил в систему: Преображенский Илья Иванович

	ИСТИНА	Войти в систему Регистрация
	ИСТИНА ПсковГУ
	Главная Поиск Статистика О проекте Помощь

ИСТИНА

ИСТИНА ПсковГУ

DLP printing of viscoelastic hydrogel/calcium phosphate composites for bone tissue replacementтезисы доклада

Прикрепленные файлы