Calcium Phosphate Powder Synthesized from Calcium Acetate and Ammonium Hydrophosphate for Bioceramics Applicationстатья
Информация о цитировании статьи получена из
Web of Science,
Scopus
Статья опубликована в журнале из списка Web of Science и/или Scopus
Дата последнего поиска статьи во внешних источниках: 26 января 2022 г.
- Авторы: Safronova Tatiana, Putlayev Valery, Filippov Yaroslav, Shatalova Tatiana, Karpushkin Evgeny, Larionov Dmitrii, Kazakova Gilyana, Shakhtarin Yury
- Журнал: Ceramics
- Том: 1
- Номер: 2
- Год издания: 2018
- Издательство: MDPI Publishing
- Местоположение издательства: Basel, Switzerland, Switzerland
- Первая страница: 375
- Последняя страница: 392
- DOI: 10.3390/ceramics1020030
- Аннотация: Calcium phosphate powder was synthesized at room temperature from aqueous solutions of ammonium hydrophosphate and calcium acetate without pH adjusting at constant Ca/P molar ratio 1.5. Phase composition of the as-synthesized powder depended on the precursors concentration: At 2.0 M of calcium acetate in the starting solution, poorly crystallized hydroxyapatite was formed, 0.125 M solution of calcium acetate afforded brushite, and the powders synthesized from 0.25–1.0 M calcium acetate solutions were mixtures of the mentioned phases. Firing at 1100 °C led to complete elimination of the reaction by-products, yet the phase composition of the annealed compacted samples was the following: When 2.0 M solution of calcium acetate was used, the obtained ceramics consisted of β-Ca3(PO4)2, whereas at 0.125 to 1.0 M of calcium acetate, the ceramics was a mixture of β-Ca3(PO4)2 and β-Ca2P2O7. Synthesized calcium phosphate powders can be used as the powdered precursors for biocompatible bioresorbable composite ceramics production. Keywords: hydroxyapatite; brushite; precipitation; tricalcium phosphate; calcium pyrophosphate; ceramic composite
- Добавил в систему: Сафронова Татьяна Викторовна
Прикрепленные файлы
| № | Имя | Описание | Имя файла | Размер | Добавлен |
|---|---|---|---|---|---|
| 1. | ceramics-01-00030-v2.pdf | ceramics-01-00030-v2.pdf | 6,7 МБ | 18 декабря 2018 [safronova] | |
| 2. | Publication_Certificate_MDPI_ceramics-01-00030.pdf | Publication_Certificate_MDPI_ceramics-01-00030.pdf | 634,9 КБ | 15 декабря 2018 [safronova] |